ZDF04防雾交联热收缩膜
当含有水份的物品需要在冷藏情况下存放或销售时，请考虑使用ZDF04防雾交联膜。ZDF04突出优点是具有消除水雾的功能，使被包装含水份物品(如肉类、水果和蔬菜等)在冷藏情况下，仍然清晰可见。
与ZDF03一样，ZDF04也采用了交联技术，因而也拥有高收缩、高强度、高韧性及耐寒等优点。ZDF04能适应所有包装机械。
常规厚度：11um、15um、19um。
开云网页版-开云(中国)-开云(中国)
性能参数
| TEST ITEM | UNIT | ASTM TEST METHOD | TYPICALVALUES | |||||||
| GAUGE 厚度 | 11um | 15um | 19um | |||||||
| TENSILE | ||||||||||
| Tensile Strength(MD) 拉伸强度 | N/mm² | D882 | 135 | 135 | 140 | |||||
| TensileStrength (TD) | 135 | 130 | 135 | |||||||
| Elongation(MD) 断裂伸长率 | % | 130 | 130 | 135 | ||||||
| Elongation(TD) | 120 | 120 | 125 | |||||||
| TEAR 撕裂强度 | ||||||||||
| MDat 400gm | gf | D1922 | 7.5 | 11.0 | 14.5 | |||||
| TDat 400gm | 8.5 | 11.5 | 15.5 | |||||||
| SEALSTRENGTH 热封强度 | ||||||||||
| MD\HotWire Seal | N/mm | F88 | 0.90 | 1.05 | 1.25 | |||||
| TD\HotWire Seal | 0.95 | 1.15 | 1.35 | |||||||
| COF(Film To Film) | - | |||||||||
| Static 静摩擦 | D1894 | 0.31 | 0.29 | 0.27 | ||||||
| Dynamic 动摩擦 | 0.3 | 0.29 | 0.28 | |||||||
| OPTICS | ||||||||||
| Haze 雾度 | D1003 | 3.9 | 4.8 | 5..4 | ||||||
| Clarity 透明度 | D1746 | 95.5 | 94.5 | 93.5 | ||||||
| Gloss@ 45Deg 光泽度 | D2457 | 81.5 | 79.0 | 77.0 | ||||||
| Antifog arrival time at5℃ 防雾起始时间 | 2hours | |||||||||
| AntifogEffect 防雾效果 | Completetransparent, no visible water 清晰透明无明显水珠 | |||||||||
| BARRIER 阻隔性 | ||||||||||
| OxygenTransmission Rate 透氧率 | cc/㎡/day | D3985 | 9900 | 8600 | 6200 | |||||
| Water Vapor Transmission Rate 透水气率 | gm/㎡/day | F1249 | 30.7 | 27.3 | 19.5 | |||||
| SHRINKAGE PROPERTIES 收缩性 | MD | TD | ||||||||
| Free Shrinkage 收缩率 | 100℃ | % | D2732 | 20 | 30 | |||||
| 110℃ | 38 | 45 | ||||||||
| 120℃ | 62 | 64 | ||||||||
| 130℃ | 81 | 78 | ||||||||
| MD | TD | |||||||||
| Shrink Tension 收缩张力 | 100℃ | Mpa | D2838 | 2.15 | 2.50 | |||||
| 110℃ | 2.80 | 3.90 | ||||||||
| 120℃ | 3.30 | 4.15 | ||||||||
| 130℃ | 3.10 | 3.85 | ||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.
以上资料是本公司内部评测之数据，仅供参考。